ASTM A90/A90M(). Standard Test Method for Weight [Mass] of Coating on Iron and Steel Articles with Zinc or Zinc-Alloy Coatings. ASTM A ZINC PLATING WEIGHT ON STEEL. This test method covers procedures for determining the weight [mass] of coating on iron or steel sheet, wire, and. A. ASTM A90 – Standards Test Method for Weight of Coating on F. ASTM A — Steel Sheet, Zinc Coated (Galvanized) or Zinc-Iron Alloy.

Author: Kigat Dut
Country: Mauritania
Language: English (Spanish)
Genre: History
Published (Last): 1 May 2007
Pages: 411
PDF File Size: 7.42 Mb
ePub File Size: 8.84 Mb
ISBN: 376-8-86830-131-1
Downloads: 15786
Price: Free* [*Free Regsitration Required]
Uploader: Nill

Current edition approved April 1, A number in parentheses indicates the year of last reapproval.

Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at the above address or at phonefaxor service astm. A asstm of zinc on iron or steel articles provides protection against corrosion. For specific hazards statements see 5.

For results to be reported in metric units, the specimen should have an area of mm2 of sheet Unless otherwise indicated, it is intended that all reagents shall conform to the speci?

The weight [mass] of coating in grams on a specimen of that area is numerically equal to the weight [mass] of coating in ounces per square foot of sheet. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of aatm of such rights, are entirely their own responsibility.

The same solution s90 be used repeatedly until the time required for stripping becomes inconveniently long.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. Except as otherwise provided, the specimens should have a minimum area of 3 in. A coating of zinc on iron or steel articles provides protection against corrosion. If specimens were prepared to the dimensions as provided in Note 2, they shall be presumed to have an area of 5.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. A fume hood is recommended for large numbers of samples atsm where the test is to be carried out frequently over extended periods of time.

  APFC EXAM SYLLABUS PDF

This standard has been approved for use by agencies of the Department of Defense. Under no circumstances should the water be added to the acid.

Originally approved in Precision and Bias Determine the weight [mass] of the specimens again, to the same precision as in the axtm determination. When it is not possible to determine the area accurately, as in specimens from corrugated sheets, the thickness of the stripped sheet shall be determined to the nearest 0.

ASTM A90/A90M 13镀锌和镀锌合金钢铁制品镀层重量的试验方法_百度文库

See Table 1 for a statistical summary of the test results. After determining the weight [mass], immerse each specimen singly in the stripping solution and allow to remain until the violent evolution of hydrogen has ceased, and only a few bubbles are being evolved. Your comments will receive asm consideration at a meeting of the responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below.

For very small items, several pieces may have to be stripped to obtain the minimum area. Historical Version s – view previous versions of standard.

The mixing should be performed under an acid fume hood. Link to Active This link will always route to the current Active version of the standard. This requires about 15 to 30 s, except in the case of sherardized coatings, which require a somewhat longer time. Mixing must be done by slowly adding sulfuric acid adtm water due to the heat generated and possible splashing.

The specimen of wire may be of any length over 12 in.

ASTM A90 – ZINC PLATING WEIGHT ON STEEL

In the body of this test method, reference to zinc coating shall be interpreted to also include zinc alloy coating except where speci?

In the body of this test method, reference to zinc coating shall be interpreted to also include zinc alloy coating except where specifically stated otherwise. Coating weights [masses] on all zinc-coated articles other than sheets are expressed in weight [mass] per unit area of surface. No further reproductions authorized. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  CAD CAM BY GROOVER AND ZIMMER PDF

ASTM A90/A90M – 13(2018)

SR means the standard deviation for R reproducibility. Certain portions of the procedure involving determination of specimen weight [mass] have traditionally been performed in SI units, and corresponding inch-pound units aatm not included. Permission rights to photocopy the standard may also be secured from the ASTM website www.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every? Therefore, the test should be performed under conditions of adequate ventilation. Since the density of the steel is known 0. NOTE 2—For convenience in calculating test results in inch-pound units, the specimen should have an area of 5.

After stripping, wash the specimens by scrubbing them under running water, dip in hot water, and wipe or blow dry. Specifications for zinc-coated articles frequently provide for different classes of coating so that the purchaser can select the coating weight [mass] most suitable to his needs.

As the protection is provided by sacri?

It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Where a continuous length is not available, shorter lengths totaling over 12 in. Each of ten laboratories tested three replicates of two different materials. Certain portions of the procedure involving determination of specimen weight [mass] have traditionally been performed aatm SI units, and corresponding inch-pound units are not included.

Hydrochloric acid fumes are present, and hydrogen gas is evolved in the stripping process. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters. Alternatively, for specimens of uniform thickness of base metal, such as a piece of plate or pipe, determine the average thickness of the stripped specimen to the nearest 0.